|Table of Contents|

Corrosion damage of bridge pile foundations under dry-wet cycles in strong salt marsh areas(PDF)

《交通运输工程学报》[ISSN:1671-1637/CN:61-1369/U]

Issue:
2023年06期
Page:
156-167
Research Field:
道路与铁道工程
Publishing date:
2023-12-30

Info

Title:
Corrosion damage of bridge pile foundations under dry-wet cycles in strong salt marsh areas
Author(s):
FENG Zhong-ju1;  CHEN Hui-yun1; 2;  WANG Fu-chun1;  HU Hai-bo3;  XU Zhan-hui4;  YAO Xian-hua5
Keywords:
bridge engineering;  strong salt marsh area;  corrosion damage mechanism of pile foundation;  indoor dry-wet cycle test;  corrosion resistance coefficient
PACS:
U446.1
DOI:
10.19818/j.cnki.1671-1637.2023.06.009
Abstract:
To investigate the damage mechanism of concrete material of bridge pile foundations under the action of dry-wet cycles and strong salt marsh corrosion, indoor simulation tests were conducted, and the mass loss rates, relative dynamic elastic moduli, and corrosion resistance coefficients of the concretes with different material mass ratios immersed in composite salt solutions with different concentrations after dry-wet cycles were studied. The corrosion resistance micro-mechanisms of the concrete in pile bodies were investigated by using a combination of scanning electron microscope(SEM), energy dispersive spectrometer(EDS), and chemical composition analysis. Research results indicate that the increase in concrete mass after dry-wet cycles is due to the formation of expansive crystals such as calcium aluminate and Friedel's salt in the material. The presence of chloride ions can inhibit the corrosive effect of sulfate ions on pile foundation concrete. When the composite salt solution concentration is different, after 120 dry-wet cycles, for the pile foundation concrete specimens with a mass ratio of cement, aggregate, sand, water, fly ash, water reducer, silica fume, and expansion agent as 327:1 103:767:170:87:7:22:44(mass ratio Ⅲ), the relative dynamic elastic modulus is 92.7%, and the minimum corrosion resistance coefficient is 0.91. In comparison, the pile foundation concrete specimens without silica fume and expansion agent or only with silica fume have a maximum relative dynamic elastic modulus of 89.7% and a minimum corrosion resistance coefficient of 0.80. The pile foundation concrete specimens with mass ratio Ⅲ exhibit better corrosion resistance performance and have no internal cracks even when they are subjected to the expansion force, indicating that the addition of silica fume and expansion agent improves the corrosion resistance of pile foundation concrete while ensuring no crack appears in the pile foundation concrete. Obviously, the factors such as the category of corrosive ions must be comprehensively considered, and further optimization of mass ratio of pile foundation concrete material must be carried out based on the mass ratio Ⅲ in practical engineering. 6 tabs, 12 figs, 30 refs.

References:

[1] 尹世平,李 耀,李贺东,等.氯盐干湿循环下TRC加固钢筋混凝土柱轴心受压性能[J].中国公路学报,2017,30(6):230-238.
YIN Shi-ping, LI Yao, LI He-dong, et al. Axial compression performance of reinforced concrete column strengthened with TRC under chloride dry-wet cycles[J]. China Journal of Highway and Transport, 2017, 30(6): 230-238.(in Chinese)
[2] 甘 磊,吴 健,沈振中,等.硫酸盐和干湿循环作用下玄武岩纤维混凝土劣化规律[J].土木工程学报,2021,54(11):37-46.
GAN Lei, WU Jian, SHEN Zhen-zhong, et al. Deterioration law of basalt fiber reinforced concrete under sulfate attack and dry-wet cycle[J]. China Civil Engineering Journal, 2021, 54(11): 37-46.(in Chinese)
[3] 冯忠居,李维洲,王廷武,等.新疆板块状盐渍土工程特性[J].交通运输工程学报,2010,10(6):1-8. FENG Zhong-ju, LI Wei-zhou, WANG Ting-wu, et al. Engineering characteristics of plate-like saline soil in Xinjiang[J]. Journal of Traffic and Transportation Engineering, 2010, 10(6): 1-8.(in Chinese)
[4] NILI M, AZARIOON A, HOSSEINIAN S M. Novel
internal-deterioration model of concrete exposed to freeze-thaw cycles[J]. Journal of Materials in Civil Engineering, 2017, 29(9): 04017132.
[5] 张留俊,裘友强,张发如,等.降水入渗条件下氯盐渍土水盐迁移规律[J].交通运输工程学报,2023,23(4):116-127.
ZHANG Liu-jun, QIU You-qiang, ZHANG Fa-ru, et al. Water-salt migration rules in chlorine saline soil under precipitation infiltration[J]. Journal of Traffic and Transportation Engineering, 2023, 23(4): 116-127.(in Chinese)
[6] CHEN Hui-yun, FENG Zhong-ju, WU Min, et al. Study on the vertical bearing performances of piles on karst cave[J]. Scientific Reports, 2023, 13: 4944.
[7] 杨晓华,张莎莎,刘 伟,等.粗颗粒盐渍土工程特性研究进展[J].交通运输工程学报,2020,20(5):22-40.
YANG Xiao-hua, ZHANG Sha-sha, LIU Wei, et al. Research progress on engineering properties of coarse-grained saline soil[J]. Journal of Traffic and Transportation Engineering, 2020, 20(5): 22-40.(in Chinese)
[8] AL-AMOUDI O S B, MASLEHUDDIN M, ABDUL-AL Y A B. Role of chloride ions on expansion and strength reduction in plain and blended cements in sulfate environments[J]. Construction and Building Materials, 1995, 9(1): 25-33.
[9] LI Yao, YIN Shi-ping, LYU Heng-lin. Performance of
interface between TRC and existing concrete under a chloride dry-wet cycle environment[J]. Journal of Central South University, 2020, 27(3): 876-890.
[10] 宿晓萍,王 清.复合盐与干湿循环双重因素作用下混凝土耐久性试验[J].吉林大学学报(地球科学版),2013,43(3):851-857.
SU Xiao-ping, WANG Qing. Experiment of the concrete performance the condition of multiple salts and dry-wet cycles[J]. Journal of Jilin University(Earth Science Edition), 2013, 43(3): 851-857.(in Chinese)
[11] 韩学强,詹树林,徐 强,等.干湿循环作用对混凝土抗氯离子渗透侵蚀性能的影响[J].复合材料学报,2020,37(1):198-204.
HAN Xue-qiang, ZHAN Shu-lin, XU Qiang, et al. Effect of dry-wet cycling on resistance of concrete to chloride ion permeation erosion[J]. Acta Materiae Compositae Sinica, 2020, 37(1): 198-204.(in Chinese)
[12] 冯忠居,胡海波,王富春,等.高海拔强盐沼泽区桥梁桩基损伤现场模拟试验[J].交通运输工程学报,2019,19(3):46-57.
FENG Zhong-ju, HU Hai-bo, WANG Fu-chun, et al. Field simulation test of bridge pile foundation damage in high altitude and strong salt marsh area[J]. Journal of Traffic and Transportation Engineering, 2019, 19(3): 46-57.(in Chinese)
[13] 冯忠居,霍建维,胡海波,等.高寒盐沼泽区干湿-冻融循环下桥梁桩基腐蚀损伤与承载特性[J].交通运输工程学报,2020,20(6):135-147.
FENG Zhong-ju, HUO Jian-wei, HU Hai-bo, et al. Corrosion damage and bearing characteristics of bridge pile foundations under dry-wet-freeze-thaw cycles in alpine salt marsh areas[J]. Journal of Traffic and Transportation Engineering, 2020, 20(6): 135-147.(in Chinese)
[14] 冯忠居,陈思晓,徐 浩,等.基于灰色系统理论的高寒盐沼泽区混凝土耐久性评估[J].交通运输工程学报,2018,18(6):18-26. FENG Zhong-ju, CHEN Si-xiao, XU Hao, et al. Durability evaluation of concrete in alpine salt marsh area based on gray system theory[J]. Journal of Traffic and Transportation Engineering, 2018, 18(6): 18-26.(in Chinese)
[15] PILEHVAR S, SZCZOTOK A M, RODRIGIEZ J F, et al. Effect of freeze-thaw cycles on the mechanical behavior of geopolymer concrete and Portland cement concrete containing micro-encapsulated phase change materials[J]. Construction and Building Materials, 2019, 200(10): 94-103.
[16] 王海龙,董宜森,孙晓燕,等.干湿交替环境下混凝土受硫酸盐侵蚀劣化机理[J].浙江大学学报(工学版),2012,46(7):1255-1261.
WANG Hai-long, DONG Yi-sen, SUN Xiao-yan, et al. Damage mechanism of concrete deteriorated by sulfate attack in wet-dry cycle environment[J]. Journal of Zhejiang University(Engineering Science), 2012, 46(7): 1255-1261.(in Chinese)
[17] 姚贤华,冯忠居,王富春,等.复合盐浸下多元外掺剂-混凝土抗干湿-冻融循环性能[J].复合材料学报,2018,35(3):690-698.
YAO Xian-hua, FENG Zhong-ju, WANG Fu-chun, et al. Property of multiple admixture-concrete in multi-salt soaking under wetting-drying and freezing-thawing cycles[J]. Acta Materiae Compositae Sinica, 2018, 35(3): 690-698.(in Chinese)
[18] 孙迎召,牛荻涛,姜 磊,等.干湿循环条件下混凝土硫酸盐侵蚀损伤分析[J].硅酸盐通报,2013,32(7):1405-1409. SUN Ying-zhao, NIU Di-tao, JIANG Lei, et al. Damage layer thickness of concrete under wet/dry cycling measured by ultrasonic method[J]. Bulletin of the Chinese Ceramic Society, 2013, 32(7): 1405-1409.(in Chinese)
[19] FIROUZI A, ABDOLHOSSEINI M, AYAZIAN R. Service life prediction of corrosion-affected reinforced concrete columns based on time-dependent reliability analysis[J]. Engineering Failure Analysis, 2020, 117: 104944.
[20] 高润东,赵顺波,李庆斌,等.干湿循环作用下混凝土硫酸盐侵蚀劣化机理试验研究[J].土木工程学报,2010,43(2):48-54.
GAO Run-dong, ZHAO Shun-bo, LI Qing-bin, et al. Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles[J]. China Civil Engineering Journal, 2010, 43(2): 48-54.(in Chinese)
[21] 姜 磊,牛荻涛.硫酸盐侵蚀与干湿循环下混凝土本构关系研究[J].中国矿业大学学报,2017,46(1):66-73.
JIANG Lei, NIU Di-tao. Study of constitutive relation of concrete under sulfate attack and drying-wetting cycles[J]. Journal of China University of Mining and Technology, 2017, 46(1): 66-73.(in Chinese)
[22] 刘道维,刘本义,李向东,等.硫酸盐和干湿循环耦合作用下混凝土性能研究[J].水利水运工程学报,2015(4):69-74.
LIU Dao-wei, LIU Ben-yi, LI Xiang-dong, et al. Property analysis of concrete under coupling action of sulfate and wet-dry cycles[J]. Hydro-Science and Engineering, 2015(4): 69-74.(in Chinese)
[23] FENG Zhong-ju, HUO Jian-wei, HU Hai-bo, et al. Research on corrosion damage and bearing characteristics of bridge pile foundation concrete under a dry-wet-freeze-thaw cycle[J]. Advances in Civil Engineering, 2021, 2021: 1-13.
[24] BASSUONI M T, NEHDI M L. Durability of self-consolidating concrete to sulfate attack under combined cyclic environments and flexural loading[J]. Cement and Concrete Research, 2009, 39(3): 206-226.
[25] GAO Jian-ming, YU Zhen-xin, SONG Lu-guang, et al.
Durability of concrete exposed to sulfate attack under flexural loading and drying-wetting cycles[J]. Construction and Building Materials, 2013, 39: 33-38.
[26] 乔宏霞,周茗如,何忠茂,等.硫酸盐环境中混凝土的性能研究[J].应用基础与工程科学学报,2009,17(1):77-84.
QIAO Hong-xia, ZHOU Ming-ru, HE Zhong-mao, et al. Research on performance of concrete in sulfate environment[J]. Journal of Basic Science and Engineering, 2009, 17(1): 77-84.(in Chinese)
[27] 冯忠居,郭穗柱,孟莹莹,等.盐沼泽区冻融作用下桥梁桩基腐蚀损伤模拟试验[J].哈尔滨工业大学学报,2021,53(9):69-78.
FENG Zhong-ju, GUO Sui-zhu, MENG Ying-ying, et al. Simulation test on corrosion damage of bridge pile foundation in freeze-thaw area of salt swamp[J]. Journal of Harbin Institute of Technology, 2021, 53(9): 69-78.(in Chinese)
[28] 姚贤华.高寒盐沼泽区公路桥梁桩基的力学特性及其安全评价[D].西安:长安大学,2018.
YAO Xian-hua. Mechanics properties and safety evaluation of highway bridge pile in Alpine salt marshes[D]. Xi'an: Chang'an University, 2018.(in Chinese)
[29] 余红发.盐湖地区高性能混凝土的耐久性、机理与使用寿命预测方法[D].南京:东南大学,2004.
YU Hong-fa. Study on high performance concrete in salt lake: durability, mechanism and service life prediction[D]. Nanjing: Southeast University, 2004.(in Chinese)
[30] 冯忠居,陈 露,孔元元,等.青海盐沼泽环境下混凝土现场腐蚀试验[J].长江科学院院报,2023,40(5):166-172.
FENG Zhong-ju, CHEN Lu, KONG Yuan-yuan, et al. Field corrosion test of concrete in salt swamp environment in Qinghai[J]. Journal of Changjiang River Scientific Research Institute, 2023, 40(5): 166-172.(in Chinese)

Memo

Memo:
-
Last Update: 2023-12-30